1.2360, X48CrMoV8-1-1 - alloy tool steel for cold working.
| Standard | Steel Grade | |||||||
|---|---|---|---|---|---|---|---|---|
| Chemical composition % | ||||||||
| C: | Mn: | Si: | P: | S: | Cr: | Mo: | V: | |
| DIN | 1.2360 - X48CrMoV8-1-1 - X 48 CrMoV 8-1-1 | |||||||
| 0.45 - 0.50 | 0.35 - 0.45 | 0.7 - 0.9 | <0.020 | <0.005 | 7.3 - 7.8 | 1.3 - 1.5 | 1.3 - 1.5 | |
1.2360, X48CrMoV8-1-1 - specifications and applications
Alloy tool steel with increased chromium content, average strength, high hardness, ductility and high abrasion resistance. Used for precision woodworking tools - knives, blades, cutters, handles for the paper, wood, pulp, and paper industries, as well as cold forming tools. The increased content of vanadium provides a high hardenability, which makes it possible to achieve hardness within the limits of 60 HRC.
Mechanical properities and heat treatment of steel 1.2360, X48CrMoV8-1-1:
- Hardness in annealed condition <240 HB
- Annealing in temperatures 835 - 865℃ cooling with furnace
- Stress relief annealing at 650℃ cooling the furnace
- Quenching at 1035 - 1070℃ with cooling in oil, salt bath or air
- Tempering at temperatures 100 - 600℃